Product Details:
|
| Polyaspartic Self-leveling Flooring Guide Formulation | |||||||
| Component | Polyaspartic resins and HDI trimer hardener | ||||||
| Curing method | Cure at normal temperature | ||||||
| Application | Weather resistance anti-stress flooring | ||||||
| Characters | Weather resistance, non-yellowing, anti-stress, non-solvents | ||||||
| A component | B component | ||||||
| Material | Content | Supplier | Process | Material | Content | Supplier | |
| F525 | 22 | Feiyang | Mix at room temperature | HDT-LV2 | 100 | Vencorex | |
| F420 | 12 | Feiyang | |||||
| Fumed silica HDK-N20 | 0.2 | BYK | |||||
| oxidized polyethlene wax 4200-20 | 0.3 | DISPARLON | |||||
| water absorbent oxazolidine | 2 | ICL | |||||
| dispering agent BYK163 | 1 | BYK | |||||
| defoamer BYK1790 | 0.5 | BYK | |||||
| defoamer BYK066N | 0.3 | BYK | |||||
| barium sulfate 1250 | 31.4 | From hina | |||||
| F420 pigment paste | 6 | ||||||
| F525 | 18 | Feiyang | |||||
| A3 powder | 5 | From hina | |||||
| BYK354 | 0.3 | BYK | |||||
| PMA | 1 | From hina | |||||
| Total | 100 | Total | 100 | ||||
| Ratio:A:B=3:1 | |||||||
| Specifications | Construction description | ||||||
| Pot life | 25min | Trowelling construction If humidity＞85%,stop construction |
|||||
| Solid content | 96 | ||||||
| Touch dry time 25℃ | 3hr | ||||||
| Hard dry time 25℃ | 24hr | ||||||
| Thickness | 1-2mm | ||||||
| Hardness | 65D | ||||||
| Elongation | 15% | ||||||
| Tensile strength | 15MPa | ||||||
| Resilience force | -- | ||||||
| Glossness | 90 | ||||||