Product Details:
|
| Polyaspartic Windmill Blade Putty Guide Formulation | |||||||
| Curing method | Air Dry | ||||||
| Application | Fiberglass substrate windmill blade putty | ||||||
| Characters | No VOC, fast cure, good flexibility, good grinding performance, good compatibility with epoxy. | ||||||
| A component | B component | ||||||
| Material | Content | Supplier | Process | Material | Content | Supplier | |
| F524 | 21.5 | Feiyang | Grind to fineness≤70um | Tolonate HDT | 20 | Vencorex | |
| F330 | 3 | Feiyang | GB808A-100 | 80 | Feiyang | ||
| dispersing agent | 1 | worthchem | |||||
| titanium dioxide | 10 | CA | |||||
| barium sulfate | 25 | CA | |||||
| 3A molecular sieve | 4.5 | CA | |||||
| calcium carbonate | 22.9 | CA | |||||
| talcum powder | 10 | CA | |||||
| Silane coupling agent | 1.5 | CA | |||||
| Defoamer | 0.5 | CA | |||||
| Leveling agent | 0.1 | CA | |||||
| Total | 100 | Total | 100 | ||||
| Ratio: 2:1 by quantity | |||||||
| Specifications(23℃,50%RH) | Remarks | ||||||
| Pot life | 10m | F524 can be replaced by F420, ratio of A and B need to adjust according to the equivalent weight. F524 equivalantweight is 330. F420 is 277. | |||||
| TVOC, g/L | ≤20 | ||||||
| Touch dry time | 0.5h | ||||||
| Hard dry time | 4h | ||||||
| Hardness | HB | ||||||
| Elongation | 50% | ||||||
| Adhesion,MPa | ≥12 | ||||||
| SHENZHEN FEIYANG PROTECH CORP., LTD | |||||||
| Feiyang Tech-Park, 8 Longchang Road, Bao'an Dist, 518101 Shenzhen, GD, China | Tel: +86(755)-36694812 | ||||||